●Low coefficient of friction
●Self-lubrication
●Low temperature resistant
●Corrosion resistant
●Wear Resistant
●Weatherproof
●Excellent chemical resistance
●Light-weight
●High tensile strength
●Good mechanical characteristics
Materials | UHMWPE |
Size | 1000*2000mm,1220*2440mm,or custom |
Processing Method | Mould Pressing |
Thickness | 8mm to 300mm |
Density | 0.93g/cm3 |
Molecular Weight Rate | <0.01% |
Color | white, red, yellow, green, blue ,black , or custom |
Customized | accept |
●Non-Toxic
●Low coefficient of friction
●Self-lubrication
●Low temperature resistant
●Corrosion resistant
●Wear Resistant
●Weatherproof
●Excellent chemical resistance
●Light-weight
●High tensile strength
●Good mechanical characteristics
| Test Items | Test method | Unit | Value | ||||||
| General properties | DIN 53479 | g/cm³ | 0.934 | ||||||
| Molecular weight | 10 6g/mol | 4.5 | |||||||
| Elongation at break | ISO 527 | % | > 340 | ||||||
| Tensile modulus | ISO 527 | Mpa | 1200 | ||||||
| Yield stress | ISO 527 | Mpa | 27 | ||||||
| Hardness | ISO 868 | Shore D | 67 | ||||||
| Melting temperature | DIN 53736 | °C | 135 | ||||||
| Water absorption | 24h/RT | % | <0.01 | ||||||
| Friction coefficient | 0.01-0.03 | ||||||||
UHMWPE is used where sliding abrasion occurs or where metal parts meet, causing friction or abrasion wear. It is excellent for chute and hopper liners, convey or components, wear pads, machine guides, impact surface and guide rails.
High abrasion & impact resistance
Easily machined
Almost completely inert to chemical attacks
Zero coefficient of friction
Non-caking & sticking
Good electrical properties
Performs very well in colder temperature applications
Maximum temperature: 180°F
Meets FDA standards
Water absorption < 0.01%
Customized size and color high quality waterproof engineering hdpe plastic sheet wear resistant corr
4x8 inch high quality wear resistant engineering uhmwpe board custom thickness and color uhmw polyet
Hot selling customized school football training HDPE board impact resistant rebound device rebound b