●Low coefficient of friction
●Self-lubrication
●Low temperature resistant
●Corrosion resistant
●Wear Resistant
●Weatherproof
●Excellent chemical resistance
●Light-weight
●High tensile strength
●Good mechanical characteristics
Materials | UHMWPE |
Size | 1000*2000mm,1220*2440mm,or custom |
Processing Method | Mould Pressing |
Thickness | 8mm to 300mm |
Density | 0.93g/cm3 |
Molecular Weight Rate | <0.01% |
Color | black , or custom |
Customized | accept |
●Non-Toxic
●Low coefficient of friction
●Self-lubrication
●Low temperature resistant
●Corrosion resistant
●Wear Resistant
●Weatherproof
●Excellent chemical resistance
●Light-weight
●High tensile strength
●Good mechanical characteristics
| Test Items | Test method | Unit | Value | ||||||
| General properties | DIN 53479 | g/cm³ | 0.934 | ||||||
| Molecular weight | 10 6g/mol | 4.5 | |||||||
| Elongation at break | ISO 527 | % | > 340 | ||||||
| Tensile modulus | ISO 527 | Mpa | 1200 | ||||||
| Yield stress | ISO 527 | Mpa | 27 | ||||||
| Hardness | ISO 868 | Shore D | 67 | ||||||
| Melting temperature | DIN 53736 | °C | 135 | ||||||
| Water absorption | 24h/RT | % | <0.01 | ||||||
| Friction coefficient | 0.01-0.03 | ||||||||
UHMWPE Lining sheet Features:
High abrasion and impact resistance.
UV Resistant .
Easily machined for Engineering Use .
Almost completely inert to chemical attacks.
Zero coefficient of friction.
Non-caking & sticking.
Good electrical properties.
Performs very well in colder temperature applications.
Maximum temperature: 180°F.
Water absorption < 0.01%.